нержавеющая сталь сварочная проволока ER310S 2.0 мм
Описание продукта
Item |
Stainless steel welding wire, solder wire, MIG wire , TIG wire |
Size |
Dia 0.5-5.5mm |
Material Grade |
ER307Si, ER307Ti ER308,308L,308Si,ER308LSi ER309,309L,309Si,309LSi ER316,316L,316LSi ER310,312,ER321,ER347,ER347V ER410,ER410NiMo ER304, 383, 385, 2209, 2553, 630, 209, etc. PS: The material can be customized according to your chemical composition |
Standard |
AISI/ASTM/SUS/GB/DIN/EN/BS |
Packing |
1. wooden reel package (about 200- 500KG) 2. Woven bag package. (about 50-85KG) 3.MIG plastic carcass reel (15kg per reel) 4.TIG plastic barrels(5kg or 15kg per barrel ) . |
Standard: AWS/A5.20 E70T-1 GB/T 10045 E500T-1 |
||||||
USE FOR |
Chemical composition |
Mechanics ability |
Package(kg) |
Dia of spool(mm) |
Size(mm) |
|
ER308L |
18Cr- Mainly for welding 18Cr-8Ni steel; |
C:0.064% ; Mn:1.65%; Si:0.42% ;Ni:8.33%;Cr:17.10% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 ; TIG:1.0-4.5 |
ER304L |
17Cr-8Ni;Mainly for welding 17Cr-8Ni steel; |
C:0.028% ;Mn:1.65%;Si:0.42%;Ni:8.33% Cr:17.10% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 ; TIG:1.0-4.5 |
ER308 |
19Cr-9 |
C:0.064%;Mn:1.65% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 19Cr-9Ni steel; |
Si:0.42%;Ni:10.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER308L |
20Cr-9Ni |
C:0.024%;Mn:1.65% |
Mpa 1200 |
5/12.5/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-9Ni steel; |
Si:0.42%;Ni:10.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER309 |
20Cr-13Ni |
C:0.064%;Mn:1.65% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-3Ni steel; |
Si:0.42%;Ni:14.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER309L |
20Cr-14Ni |
C:0.024%;Mn:1.65% |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-14Ni steel |
Si:0.42%;Ni:14.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER309Lsi |
20Cr-14Ni |
C:0.024%;Mn:1.65% |
Mpa1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 20Cr-4Ni steel |
Si:1.02%;Ni:14.33% Cr:20.10% |
TIG:1.0-4.5 |
||||
ER321 |
16Cr-7Ni |
C:0.064%;Mn:1.65% Si:0.42%; |
Mpa 1200 |
5/10/15/20 |
100/270/300 |
MIG:0.8-1.6 |
Mainly for welding 16Cr-7Ni steel |
Ni:8.33% Cr:17.10% Ti:0.73% |
TIG:1.0-4.5 |
||||
ER347 |
16Cr-9Ni |
C:0.064%;Mn:1.65% Si:0.42%; |
Mpa 1200 |
5/10/15/20 |
100/270/300 0 |
MIG:0.8-1.6 |
Mainly for welding 16Cr-9Ni steel |
Ni:9.33% Cr:17.10% |
TIG:1.0-4.5 |
||||
(Ta+Nb(10*C)-10 |